Solvent composition for cleaning silicon wafers

Description Submit all comments and votes

This invention relates, as indicated, to an improved solvent composition especially useful in cleaning and drying silicon wafers.

BACKGROUND OF THE INVENTION AND PRIOR ART

In the production of integrated circuits, "chips" formed of silicon metal and on which are etched intricate circuits, are an essential component. The silicon wafers are carefully cut from a single crystal of silicon. These wafers are about 2" in diameter. In the processing of these wafers they become contaminated with dirt, dust, grease, etc. Before further processing into the final "chips" the wafers must be carefully cleaned.

In the semiconductor industry, wafers are rinsed in water after many process steps and, as indicated, then carefully cleaned and dried prior to the continuation of the fabrication process. At the present time, the silicon wafers are placed in a "boat" and dipped or sprayed with deionized water. The boats are subsequently loaded into a high speed centrifuge where the wafers are spin-dried. Recent technology has made use of vapor dryers utilizing isopropyl alcohol as a drying agent. The method creates a significant amount of waste over the period of a month, for example, and also a significant fire hazard.

It was desired, therefore, to develop a solvent system that was easily recovered and recycled, had excellent cleaning properties, had a convenient boiling point in the range of from about 40.degree. to 120.degree. C. and a very high, or no flash point. It was found that these criteria were met with a solvent composition which is a mixture of a fluorocarbon or chlorofluorocarbon, and a partially fluorinated alcohol. The system is unique especially for cleaning silicon wafers in that the acidic nature of the alcohol provides excellent cleaning, and the fluorocarbon or fluorochlorocarbon aids in drying the wafer without leaving any residue. The vapor may be recovered, condensed and reused.

The compositions hereof are used in the usual manner of rinsing in a boat or in a hot vapor system and then heating to a temperature sufficient to volatilize the solvent. Centrifuging may be used, but is unnecessary.

Reference may be had to Japanese Kokais Nos. 61/255977 and 58/122980. The former thermally stabilizes a working medium including a hydrocarbon (e.g., methane, ethane, propane, n-butane, isobutane, n-pentane, isopentane, n-hexane or n-heptane,) alcohol, e.g., methanol, ethanol, 2,2,2-trifluoroethanol or 2,2,2,3,3-pentafluoropropanol, a mixture of fluorinated alcohol and water or ammonia, 4-8C perfluoroalkane, or freon, an azeotropic mixture of CCl.sub.2 F.sub.2 and CHF.sub.2 --CH.sub.3 or azeotropic mixture of CHClF.sub.2 and CClF.sub.2 CF.sub.3. To the working medium is added phosphine sulfide and glycidyl ether and optionally lubricating oil. This composition is used to treat steel, aluminum, aluminum alloy, or brass.

The latter Japanese Kokai teaches a processing fluid for use in a heat transfer device of a closed fluid cycling system with evaporation and condensing sections. The processing fluid is composed of trifluoroethanol and contains up to a maximum of 15% water. The fluid used contains water, ethanol, freon, mercury, cesium, pentane and heptane.

Each of these compositions is used for a different purpose and in a different manner.

BRIEF STATEMENT OF THE INVENTION

Briefly stated, the present invention is in a nonaqueous solvent composition especially useful for cleaning and drying silicon wafers. The solvent consists essentially of (a) from about 30 to about 90 parts by weight of a haloalkylhydrocarbon containing from 1 to 10 carbon atoms, and (b) from about 10 to about 70 parts by weight of a partially fluorinated alcohol containing from 2 to 4 carbon atoms. Normally, components (a) and (b) total 100 parts, although insignificant amounts of volatile other components may be present so long as they do not adversely affect the ability of the solvent to achieve its intended purpose. The amounts of such materials are generally less than 5 parts in 100 parts and preferably less than 0.1 part in 100 parts.

DETAILED DESCRIPTION OF THE INVENTION

As indicated above, the solvent compositions of the present invention contain two essential ingredients. One of these (hereinafter referred to as component (a)) is a haloalkylhydrocarbon containing from 1 to 12 carbons atoms. For most purposes, these haloalkylhydrocarbons are perhalogenated, that is, all the hydrogen atoms are replaced with a halogen, preferably fluorine and/or chlorine. Thus, mixed fluorochlorohydrocarbons are contemplated hereby.

The second essential component (hereinafter referred to as component (b)) is a relatively low molecular weight partially fluorinated alcohol containing from 2 to 4 carbon atoms. These alcohols contain carbon, hydrogen, fluorine and oxygen as the only elements therein.

Component (a) is present in the solvent compositions hereof in an amount of from about 30 parts to about 90 parts by weight per 100 parts of solvent. For most purposes, component (a) is the major component although as will be seen from the examples below, it may be the minor component.

Component (b) is the component primarily responsible for the cleaning action of the solvent compositions hereof. It is generally present in an amount of from about 10 to about 70 parts by weight based on 100 parts of solvent. For most purposes, component (b) is the minor component although as will be seen from the specific examples below, it may be the major component.

Components (a) and (b) are normally and preferably single compounds. However, it is contemplated hereby that two or more materials qualifying as component (a) ingredients, and two or more materials qualifying as component (b) may be used in place of the single compound. Thus, the solvent compositions hereof may have components (a), (a') and (b); (a), (a'), (b) and (b'); (a), (b), and (b'), as well as the preferred (a) and (b), the prime (') indicating another member of the same class.

The compositions of (a) and (b) may be standing absorb minor amounts of moisture not to exceed about 5 parts by weight. Such insignificant amounts of moisture are not deleterious to the compositions hereof, and may, although it is not recommended, be added in amounts up to 1 parts or 2 parts per 100 parts of solvent prior to use. The compositions initially are preferably nonaqueous. Other ingredients in very minor amounts, less than 5 parts/100 parts by weight such as low boiling alcohols, ethers, ketones and esters may also be included.

Both components (a) and (b) desirably contain fluorine. Component (a) may, therefore, have the general formula:

C.sub.n F.sub.2n+2-x Cl.sub.x

wherein n is a whole number from 1 to 12, and x is a number from 0 to 2n. Preferably, n is from 2 to 6, and x is preferably from 0 to 4.

Specific examples of component (a) include, but are not limited to the following:

Trichlorofluoromethane

Dichlorodifluoromethane

Chlorotrifluoromethane

Tetrafluoromethane

1,1,2,2-tetrachloro-1,2-difluoroethane

1,1,2-trichloro-1,2,2-trifluoroethane

1,2-dichloro-1,1,2,2-tetrafluoroethane

Chloropentafluoroethane

Hexafluoroethane

1,1,1,3-tetrachloro-2,2,3,3-tetrafluoropropane

1,1,1-trichloro-2,2,3,3,3-pentafluoropropane

Octafluoropropane

tetrachloroperfluorobutane

1,1-dichlorodecafluoropentanes

1,1,1-trichloroundecafluorohexanes

Dodecafluorocyclohexane

Tetradecafluorohexanes

Perfluoroheptanes

Perfluorohexanes

Perfluorooctanes

Perfluorodecanes

Perfluorododecanes

Specific examples of partially fluorinated alcohols contain carbon, hydrogen, fluorine and oxygen, the latter atom as part of an --OH group, and include:

Trifluoroethanol

3,3,3-trifluoropropanol

4,4,4-trifluorobutanol

2-fluoroethanol

2,3,3,3-tetrafluoropropanol

2,2,3,3-tetrafluoropropanol

4-fluorobutanol

2,2-difluoropropanol

1,1-difluoroethanol-2

3,3-difluoropropanol

1,1-difluoropropanol-3

3-fluoropropanol

1-monofluoropropanol-3

2,2,3,3,3-Pentafluoropropanol

1,1,1,2,2-Pentafluoropropanol-3

As above indicated, components (a) and (b) are simply mixed together to formulate the solvent compositions of the present invention. Typical examples of such solvent compositions are:

______________________________________ EXAMPLE 1 Perfluoroheptane 70 parts Trifluoroethanol 30 parts EXAMPLE 2 1,1,2-trichloro-1,2,2-trifluoroethane 30 parts Trifluoroethanol 70 parts EXAMPLE 3 1,1,2-trichloro-1,2,2-trifluoroethane 50 parts Trifluoroethanol 50 parts EXAMPLE 4 1,1,2-trichloro-1,2,2-trifluoroethane 90 parts Trifluoroethanol 10 parts EXAMPLE 5 Tetrochloroperfluorobutane 30 parts 3,3,3-trifluropropanol 70 parts EXAMPLE 6 Tetrachloroperfluorobutanes 60 parts Trifluoroethanol 40 parts EXAMPLE 7 Tetrachloroperfluorobutanes 90 parts Trifluoroethanol 10 parts EXAMPLE 8 Perfluorohexane 70 parts 3,3,3,-trifluoropropanol 30 parts EXAMPLE 9 Perfluorohexanes 45 parts 2,2,3,3-tetrafluoropropanol 55 parts EXAMPLE 10 Perfluorohexanes 10 parts Trifluoroethanol 90 parts EXAMPLE 11 Perfluorodecanes 60 parts Trifluoroethanol 40 parts EXAMPLE 12 Perfluoroheptanes 70 parts Trifluoroethanol 20 parts 3,3,3-trifluoropropanol 10 parts EXAMPLE 13 Perfluoroheptanes 35 parts Perfluorohexanes 35 parts Trifluoroethanol 30 parts EXAMPLE 14 Tetrachloroperfluorobutane 25 parts Perfluorohexanes 25 parts 3,3,3-trifluoropropanol 20 parts Trifluoroethanol 30 parts EXAMPLE 15 Trifluoroethyltrifluoroacetate 0 to 5 parts Perfluoroheptane 70 parts Trifluoroethanol 30 parts EXAMPLE 16 Perfluoroheptane 70 parts 2,2,3,3,3-tetrafluoropropanol 30 parts EXAMPLE 17 Perfluoroheptane 80 parts 2,2,3,3,3-pentafluoropropanol 20 parts ______________________________________

The foregoing examples are illustrative of the manner of composing the compositions of the present invention. The ingredients are generally mutual solvents for each other and hence no special techniques are involved in mixing the proper proportions of the components. The compositions are generally stable and, if necessary may be heated slightly to aid in dissolution of the ingredients. and to prevent stability in use.

* * * * *