Cleaning composition based on 1,1,1,2,2-pentafluoro-3,3-dichloropropane and methyl tert-butyl ether

Description Submit all comments and votes

FIELD OF THE INVENTION

The present invention relates to the area of chlorofluorinated hydrocarbons and more particularly to a novel composition exhibiting an azeotrope which can be used as a cleaning and degreasing agent for solid surfaces, in particular for removing flux and low-temperature cleaning of printed circuits.

BACKGROUND OF THE INVENTION

1,1,2-Trichloro-1,2,2-trifluoroethane (known in the art under the name F113) is widely used in industry for cleaning and degreasing solid surfaces. Apart from its application in electronics for cleaning soldering fluxes so as to remove any flux still adhering to the printed circuits, its application in degreasing heavy metal parts and for cleaning high-quality, high-precision mechanical parts, such as, for example, gyroscopes and military or aerospace equipment may be mentioned. In its various applications, F113 is most often combined with other organic solvents (for example methanol), preferably in the form of azeotropic or pseudoazeotropic mixtures which do not separate and when being refluxed have essentially the same composition in the vapor phase as in the liquid phase.

However, F113 is one of the completely halogenated chlorofluorocarbons which are currently suspected of attacking and decomposing stratospheric ozone.

DESCRIPTION OF THE INVENTION

As a contribution to solving this problem, the present invention proposes to replace the compositions based on F113 by a novel composition based on methyl tert-butyl ether (thereafter MTBE) and 1,1,1,2,2-pentafluoro-3,3-dichloropropane. The latter compound, known in the art under the name 225ca, is virtually devoid of any destructive effect with respect to ozone.

The composition to be used according to the invention comprises 55 to 80% by weight of 225ca and 20 to 45% of MTBE. This range gives rise to an azeotrope whose boiling temperature is 59.9.degree. C. at standard atmospheric pressure (1.013 bar), while the composition according to the invention has pseudoazeotropic behavior, i.e., the composition of the vapor phase and liquid phase is essentially the same, which is particularly advantageous for the intended applications. Preferably, the 225ca content is chose from between 62 and 67% by weight and that of MTBE from between 38 and 33% by weight.

The 225ca/MTBE azeotrope is a negative azeotrope, because its boiling point (59.9.degree. C.) is above that of the constituents (225ca:51.1.degree. C.; MTBE:54.degree. C.).

Similar to the known compositions based on Fl13, the composition according to the invention can be advantageously stabilized against hydrolysis and/or attack by free radicals, which are likely to occur during the cleaning process, by adding a conventional stabilizer, such as, for example, nitromethane, propylene oxide or a mixture of these compounds, the proportion of the stabilizer ranging from 0.01 to 5%, relative to the total weight of 225ca +MTBE.

The composition according to the invention can be used for the same applications and using the same techniques as the former compositions based on F113.

EXAMPLES

The examples which follow illustrate the invention without limiting it.

EXAMPLE 1 : DETECTION OF THE AZEOTROPE

100 g of MTBE and 100 g of 225ca are introduced in the bottom of a distillation column (30 plates). The mixture is then refluxed for one hour to bring the system to equilibrium. After reaching a steady temperature (59.9.degree. C.), a fraction (about 50 g) is removed and analyzed by gas-phase chromatography.

The test results shown in the table below indicate the presence of a 225ca/MTBE azeotrope.

______________________________________ COMPOSITION (% by weight) 225ca MTBE ______________________________________ Initial mixture 50 50 Fraction removed 64.5 35.5 ______________________________________

EXAMPLE 2: VERIFICATION OF THE AZEOTROPIC COMPOSITION

200 g of a mixture comprising 64.5% by weight of 225ca and 5.5% by weight of MTBE are introduced into the boiler of an adiabatic distillation column (30 plates). The mixture is then refluxed for one hour to bring the system to equilibrium, and a fraction of about 50 g is then removed and it is then analyzed by gas-phase chromatography. The results listed in the table below show the presence of a negative azeotrope, because its boiling point is above that of the pure constituents: 225ca and MTBE.

______________________________________ COMPOSITION (% by weight) 225ca MTBE ______________________________________ Initial mixture 64.5 35.5 Fraction collected 64.5 35.5 Still bottom 64.4 35.6 ______________________________________

Boiling temperature corrected for 1.013 bar: 59.9.degree. C.

When employed for cleaning soldering flux or degreasing mechanical parts, this azeotrope gives results which are as good as those of the compositions based on F113 and methanol.

EXAMPLE 3: CLEANING-OFF OF SOLDERING FLUX

200 g of the azeotropic 225ca/MTBE composition are introduced into an Annemasse ultrasonic bath, and the mixture is then brought to the boiling temperature.

Glass plates which are coated with soldering flux and have been heated in an oven at 220.degree. C for 30 seconds are immersed in the boiling ultrasonic liquid for 3 minutes and then rinsed in the vapor phase for 3 minutes.

After drying in air, inspection using low-angle illumination reveals a complete absence of any residual soldering flux. Thus, the same result was obtained as when using an F113/methanol (93.7%/6.3%) composition.

Although the invention has been described in conjunction with specific embodiments, it is evident that many alternatives and variations will be apparent to those skilled in the art in light of the foregoing description. Accordingly, the invention is intended to embrace all of the alternatives and variations that fall within the spirit and scope of the appended claims.

* * * * *