Description  |
|
|
This is a continuation-in-part of Application PCT/EP
9101909, filed Oct. 8, 1991, now pending.
This invention relates to one-component silicone systems (hereinafter referred to as 1-C-RTV compounds) which cure rapidly under the effect of moisture with elimination of certain carbonamides, develop good adhesion to many substrates in the
process and give vulcanizates that are stable under extreme climatic conditions.
There have already been numerous publications on the subject of 1-C-RTV compounds which cure with elimination of carbonamides, of for example DE-A 1 224 039, 1 247 646, 1 258 087 and 3 114 773 and EP-A 22 976. The products claimed therein are
generally distinguished by good adhesion to many substrates and show good stability in storage in the unvulcanized state. In most cases, however, they cure relatively slowly to form products of low hardness and are therefore only suitable to a limited
extent for applications requiring rapid vulcanization to elastomers of high hardness. The compounds described in DE-A 3 114 773 come relatively close to the desired behavior standard. However, all the embodiments described therein are attended by the
disadvantage that the vulcanizates produced from them can change under the effect of elevated temperature and atmospheric moisture, so that they can only be used to a limited extent for applications involving exposure to extreme climatic conditions.
The present invention relates to one-component silicone systems vulcanizable under the effect of moisture based on a mixture of
(A) typical hydroxy-terminated polydimethyl siloxanes having a viscosity of 1 to 100 Pa.s,
(B) optionally plasticizers,
(C) typical fillers,
(D) a dialkyl tin(IV) catalyst, characterized by a content--per 100 parts by weight (A)--of
(E) 2 to 30 parts by weight of a silane having the composition
in which
X is either ##STR1## and (F) 0.1 to 5 parts by weight of an aminoalkyl alkoxysilane containing one or more basic nitrogen atoms connected to a silicon atom by at least 3 carbon atoms,
the molar ratio of components (E) to (F) being at least 2.5.
Components (E) and (F) are preferably used in such quantities that the molar ratio does not fall below 3.
The molar ratio should preferably not exceed 10 and, more preferably, should not exceed 6.
It has now surprisingly been found that rapidly curing 1-C-RTV compounds which show good adhesion and excellent stability to extreme weathering influences can be obtained using the above-mentioned starting materials in the quantitative ratios
indicated.
An .alpha.,.omega.-bis-(trimethylsiloxy)-polydimethyl siloxane having a viscosity of 0.01 to 10 Pa.s is preferably used as the plasticizer (B) in a quantity of, preferably, 0 to 100 parts by weight and, more preferably, 30 to 100 parts by weight,
based on 100 parts by weight of component (A).
The polysiloxanes mentioned as components (A) and (B) correspond to the prior art and may be obtained by known methods. According to the invention, they may even be replaced by other polymer raw materials corresponding to the prior art, for
example by polysiloxanes containing other substituents in addition to methyl radicals. Phenyl or vinyl radicals are mentioned as examples of such substituents. Organic polymers, in particular aromatic or aliphatic hydrocarbons which are predominantly
branched may also be used as the plasticizer component instead of the polysiloxanes mentioned under (B).
The amidosilanes (E) may be obtained from methyl ethoxydichlorosilane and N-methyl benzamide or .epsilon.-caprolactam in the presence of bases by known methods, for example by the method described in DE-A 1 247 646.
Suitable fillers (C) are reinforcing fillers, such as pyrogenic or precipitated silica and carbon black, and carbonate-, silicate- or oxide-containing minerals with little or no reinforcing effect. The surfaces of the fillers may be pretreated.
Silanized pyrogenic silicas and ground natural chalks or precipitated chalks coated with stearic acid are particularly preferred. It is particularly preferred to use 60 to 120 parts by weight chalk and 10 to 30 parts by weight pyrogenic silica, based in
each case on 100 parts by weight component (A).
Suitable tin catalysts (D) are dialkyl tin carboxylates, for example dibutyl tin acetate, dibutyl tin dilaurate, dibutyl tin bis-(2-ethylhexanoate). Alternatively, the corresponding dioctyl derivatives may be used. In addition, dialkkyl tin
oxides, such as dibutyl tin oxide or dioctyl tin oxide, are present in solutions with aminoalkyl alkoxysilanes (F), as described in EP application 88 117 221.7 for oxime-curing 1-C-RTV compounds, have proved to be particularly suitable.
Suitable aminoalkyl alkoxysilanes (F) are such compounds as H.sub.2 NCH.sub.2 CH.sub.2 CH.sub.2 Si(OC.sub.2 H.sub.5).sub.3, H.sub.2 NCH.sub.2 CH.sub.2 NHCH.sub.2 CH.sub.2 CH.sub.2 Si(OCH.sub.3).sub.3, H.sub.2 NCH.sub.2 CH.sub.2 CH.sub.2
SiCH.sub.3 (OC.sub.2 H.sub.5).sub.2 and HN[CH.sub.2 CH.sub.2 CH.sub.2 Si(OC.sub.2 H.sub.5).sub.3 ].sub.2. Other compounds of this type have been described as primers or crosslinking agents for silicone pastes, cf. for example US-A 3,888,815.
In the same way as known 1-C-RTV compounds, the compounds according to the invention may be produced in planetary mixers, butterfly mixers, dissolvers, continuous mixing screws or other machines suitable for the production of pastes. The
compounds have to be protected against atmospheric moisture during production and storage. For the production of particularly reactive embodiments, the compounds may have to be mixed and packed in a dry inert gas atmosphere.
The invention is
illustrated by the following Examples.
EXAMPLE 1
32.75 Parts by weight of an .alpha.,.omega.-dihydroxypolydimethyl siloxane, viscosity 80 Pas, and 26.2 parts by weight of an .alpha.,.omega.-bis-(trimethylsiloxy)-polydimethyl siloxane, viscosity 0.1 Pas, were mixed with 0.5 part by weight
H.sub.2 NCH.sub.2 CH.sub.2 CH.sub.2 Si(OC.sub.2 H.sub.5).sub.3 in a planetary mixer. 30.0 Parts by weight of a ground natural chalk treated with stearic acid and 3.0 parts by weight of a pigment paste containing 50% TiO.sub.2 in silicone oil were then
added and dispersed, followed by the addition of 2.8 parts by weight methyl-bis-(N-methylbenzamido)-ethoxysilane, 4.5 parts by weight of a hydrophobicized pyrogenic silica and 0.25 part by weight of a solution of dibutyl tin oxide in H.sub.2 NCH.sub.2
CH.sub.2 CH.sub.2 Si(OC.sub.2 H.sub.5).sub.3 prepared in the absence of moisture at 100.degree. C. The catalyst solution had a tin content of 20%.
Glass test specimens with joint dimensions of 12 mm.times.12 mm.times.50 mm were prepared from the paste in accordance with DIN 52 455 and tested for tensile stress/elongation behavior.
______________________________________ Tensile stress at 100% elongation 0.26 MPa Ultimate tensile strength 0.33 MPa Elongation at break 200% ______________________________________
After curing for 14 days, the test specimens had a Shore A hardness (DIN 53 505) of 17. The hardness test specimens were subjected to a weathering test for 2 months at 55.degree. C. /95% relative air humidity. After subsequent storage for 1
week in a standard conditioning atmosphere, the test specimens had Shore A hardnesses of 15 to 18. There were no signs of the embrittlement which many 1-C-RTV compounds show under the described conditions.
EXAMPLE 2
32.1 Parts by weight of an .alpha.,.omega.-dihydroxypolydimethyl siloxane, viscosity 80 Pas, 26.2 parts by weight of an .alpha.,.omega.bis-(trimethylsiloxy)-polydimethyl siloxane, viscosity 0.1 Pa.s, and 0.5 part by weight H.sub.2 NCH.sub.2
CH.sub.2 NHCH.sub.2 CH.sub.2 CH.sub.2 Si(OCH.sub.3).sub.3 were mixed. 30.0 Parts by weight of the natural chalk used in Example 1 and 3.0 parts by weight of the pigment paste were then incorporated by dispersion. 3.5 Parts by weight ##STR2## 4.5 parts
by weight of the hydrophobicized pyrogenic silica and 0.20 part by weight of the tin catalyst solution used in Example 1 were then added. The testing of tensile properties were performed according to DIN 52455 as described in Example 1. The following
results were obtained:
______________________________________ Tensile stress at 100% elongation 0.24 MPa Ultimate tensile strength 0.31 MPa Elongation at break 240% ______________________________________
After the weathering test described in Example 1, there were no signs of any embrittlement.
Comparative example 1. without silane (E)
Example 1 was repeated without addition of methyl-bis(N-methyl-benzamido)ethoxysilane. In order to avoid contact with atmospheric moisture, the resulting paste was filled into cartridges. After 3 days a soft rubber had formed in the cartridges. The experiment shows that the silane (E) is necessary for the production of a one-component sealant, which is stable in the absence of moisture.
Comparative example 2. without silane (F)
Example 1 was repeated without addition of any silane (F). No H.sub.2 NCH.sub.2 CH.sub.2 CH.sub.2 Si(OC.sub.2 H.sub.5).sub.3 was added and the catalyst solution of dibutyltinoxide in H.sub.2 NCH.sub.2 CH.sub.2 CH.sub.2 Si(O)C.sub.2
H.sub.5).sub.3, which contained 20% tin, was replaced by the same quantity of dibutyltindilaurate. The product was storage stable in the absence of moisture. In contact with moisture it cured to a rubber with the following properties (DIN 52455):
______________________________________ Tensile stress at 100% elongation 0,15 MPa Ultimate tensile strength 0,16 MPa Elongation at break 110%. ______________________________________
Vulcanized samples show good resistance to extreme weathering conditions. In this respect they were comparable to the products of the original example 2 which were tested for adhesion to different substrates. Strings of the pastes were applied
on the substrates, listed below. After curing for one week under the influence of atmospheric moisture, the adhesion was evaluated qualitatively by pulling off the strings. In case of adhesive rupture, the samples were judged as having "no adhesion".
In the case of cohesive failure within the string, the material was judged as having adhesion (adhesion--yes).
______________________________________ Adhesion Example 1 Comparative Example 2 ______________________________________ Glass yes yes Tiles yes yes Aluminum yes no Iron yes no Copper yes no PVC yes no Acrylic glass yes no Polycarbonate
yes no. ______________________________________
The test demonstrates that sealants, which contain no aminosilane (F), adhere to few substrates, only. The product, according to example one, adhered to all substrates tested.
In order to prove, that the introduction of dibutyltindilaurate in comparative example 2 has no negative influence on adhesion, Example 1 was repeated with equal amounts of dibutyldilaurate, instead of a solution of dibutyltinoxide in the silane
H.sub.2 NCH.sub.2 CH.sub.2 CH.sub.2 Si(OC.sub.2 H.sub.5).sub.3. The adhesion properties of this paste were similar to the original example 1.
* * * * *
|
|
 |
|
 |
Description |
|