Description  |
|
|
BACKGROUND OF THE
INVENTION
1. Field of the Invention
The present invention relates to an optical recording medium, such as a so-called compact disk (CD) or the like and which is of such a system as to reproduce a signal by detecting a changed amount of a reflection of a reproduced light beam with
radiating from a substrate side a reproducing light on recording patterns such as concavities and convexities corresponding to an information signal recorded on a transparent substrate or recorded pits recorded by the change of optical characteristics of
the medium.
2. Description of the Related Art
Recently, in the field of information recording, researches concerning the optical information recording system have hitherto been advanced in various places. The optical information recording system has lots of advantages, such as to effect the
recording and reproducing in a non-contact fashion, to achieve high recording density which is higher than that of the magnetic recording system by one figure, to be applicable to several memory types of read-only type, write-once type, rewritable type
or the like. Therefore, this optical information recording system can realize an inexpensive large storage capacity file and a variety of uses from professional to consumer uses can be considered.
As the read-only type optical recording medium of the above-mentioned types, a digital audio disk (i.e., so-called compact disk, CD), an optical video disk (so-called laser disk, LD) or CD-ROM have already been widespread. In these optical
recording media, a reflection layer made of a metal thin film such as an A1 film or the like is deposited on the surface of a substrate having a layer in which concavities and convexities corresponding to an information signal or record patterns based on
the change of optical characteristics of the medium are formed. A reproducing light such as a laser light or the like is radiated on the optical recording medium from the transparent substrate side and information is reproduced by detecting intensity of
a reflected light.
In the optical recording medium of the above-mentioned read-only type, there is a demand that the recording density thereof is further improved in order to cope with digital VTRs, high-definition television receivers (HDTVs) or the like.
Further, there is a demand that optical recording media are miniaturized in size in order to facilitate the operation thereof. From this standpoint, a further improvement of the recording density is requested.
As means for improving the recording density of the optical recording medium, it is considered to provide smaller recording pattern corresponding to information formed on the optical recording medium. If the recording pattern were made very
small, then a spot diameter of a reproducing light that reproduces the optical recording medium would exceed a diffraction limit and the recording pattern would not be reproduced.
Therefore, in order to reduce the wavelength of the reproducing light, to compress a signal code or to improve the above-mentioned diffraction limit, there are considered various methods, such as increase of a numerical aperture (NA) of the
optical system or the like. Of these methods, a super resolution receives a remarkable attention as a powerful means.
A principle of super resolution is such that a spot diameter of the radiated light is reduced to be smaller than the diffraction limit by setting an aperture smaller than the diffraction limit of the radiated light at object point position to
thereby increase a resolution (e.g., "Charles W. McCutchenm "Super-resolution in Microscopy and the Abbe Resolution Limit." Journal of Optical Society of America, 57(10), 1190 (1967)", "Tony Wilson and Colin Shepard, "Theory and Practice of Scanning
Optical Microscopy." Academic Press (London), 1984, etc.).
If such super resolution is applied to the optical recording medium, then the aperture must be moved as the reproducing light is moved on the optical recording medium. U.S. Pat. No. 5,153,873 described a technology that an aperture smaller
than the diffraction-limited radiation spot) is formed within the reflection layer and resolution is improved by reducing the spot diameter of a reflected light reflected by the reflection layer.
In this previously-proposed method, as the optical response material, there is enumerated a non-linear optical material whose optical characteristic is directly changed by the reproducing light or a phase change material whose optical
characteristic is changed by heat generated when the reproducing light absorbs a light. However, specific proper materials are not illustrated in the above-mentioned U.S. Pat. No. 5,153,873 and cannot be realized in actual practice.
Further, the assignee of the present application has previously proposed a method (now U.S. Pat. No. 5,018,119) in which super resolution effect is realized by reducing an area of a magnetic Kerr effect of a magneto-optical recording and
reproducing system to be smaller than the spot diameter of the reproduced light thermally to thereby achieve the high density recording.
SUMMARY OF THE INVENTION
It is therefore an object of the present invention to provide an optical recording medium in which information of high recording density obtained by a recording pattern smaller than a diffraction-limited radiation spot of the reproduced light can
be reproduced by super resolution.
It is another object of the present invention to provide an optical recording medium in which information of high recording density obtained by a recording pattern smaller than a diffraction-limited radiation spot of the reproduced light can be
reproduced by super resolution and in which a reproduced signal is increased considerably.
To attain the aforesaid objects, the inventors et al. have studied vigorously optical response materials and found out that a saturable absorption dye should be used as the optical response material and that super resolution phenomenon can be
realized by an absorption saturation phenomenon occurred when a light of an ex-saturable absorption dye is irradiated.
More specifically, according to the present invention, as shown in FIG. 1A, in an optical recording medium in which a recording pattern recorded on a transparent substrate as a change of optical characteristic such as concavities or convexities
in response to an information signal is detected by the change of a reflection of a reproducing light which moves to scan the transparent substrate relatively to thereby reproduce a signal, a layer having at least a saturable absorption dye is formed on
the recording pattern, a molecular extinction coefficient .epsilon. of the saturable absorption dye in the wavelength of the reproduced light is 10.sup.4 or greater, and a relaxation time .tau. thereof falls in a range of 1 ns.ltoreq..tau..ltoreq. 100
ns.
According to the present invention, in the optical recording medium, as shown in FIG. 1B, there may be sequentially formed a transparent substrate, a saturable absorption dye containing layer and a reflection layer of which the reflectivity on
the air boundary is higher than 70%. Further, a thickness of the saturable absorption dye containing layer may be selected in such a manner as to minimize intensity of a reflected light due to interference relative to light intensity of a reproduced
light.
Further, in the optical recording medium according to the present invention, the saturable absorption dye may be naphthalocyanine-based dye.
According to the present invention, as shown in FIG. 2 which is a schematic enlarged cross-sectional view showing an example thereof, between the substrate 1 an the saturable absorption dye containing layer 2 is formed a high (low) refractive
index layer made of a material whose refractive index is relatively high (or low) as compared with those of the materials forming the substrate 2 and the saturable absorption dye containing layer 2.
Further, according to the present invention, on the substrate 1 are sequentially formed the high refractive index layer 3 and the saturable absorption dye containing layer 2 on which there is formed a reflecting layer 4 whose reflectivity on the
air boundary is 70% or greater, in that order.
According to the present invention, in the above-mentioned structure, a real portion refractive index of the high refractive index layer 3 is selected to be 1.8 or greater.
Further, in the above-mentioned structure, the high refractive index layer 3 is formed of an inorganic ceramic material formed by a vacuum thin film forming method.
Furthermore, in the above-mentioned structure, the inorganic ceramic material is formed as a mixed film of ZnS and SiO.sub.2.
In the optical recording medium according to the present invention, apertures smaller than diffraction limit of a reproduced light by changing a complex index of refraction at very small portion of the saturable absorption dye containing layer
are formed with radiation of the reproducing light on the saturable absorption dye containing layer, thereby realizing super resolution phenomenon. In this case, the saturable absorption dye in the saturable absorption dye containing layer is changed
from a ground state to an excited state in which a complex index of refraction is changed by the absorption of the reproduced light to form apertures. Then, the saturable absorption dye is returned to the ground state through the relaxation time .tau..
Therefore, if a molecular extinction coefficient .epsilon. of the saturable absorption dye used in the wavelength of the reproduced light is set to be .epsilon.<10.sup.4, then when the thickness of the saturable absorption dye containing
layer is selected so as to substantially minimize the reflection intensity due to interference relative to the light intensity of the reproduced light, it is not possible to obtain a sufficient sensitivity. If the relaxation time .tau. of the saturable
absorption dye in the wavelength of the reproduced light is set to be .tau.< 1 ns, then an aperture forming time is too short to obtain a sufficient sensitivity. If the relaxation time .tau. is set to be 100 ns <.tau., then the aperture forming
time is so long that a shape of aperture becomes elliptical which is long in the scanning direction of the reproduced light. As a result, a resolution cannot be improved. Incidentally, if the relaxation time .tau. is set in a range of from 1 s to 10
ns, there can then achieved a larger effect.
The saturable absorption dye should preferably be dye which has a strong absorption in a laser wavelength region (750 to 810 nm) because a laser light is frequently used as a reproducing light. Further, the saturable absorption dye should
preferably be such one that is stable from a thermal and photochemical standpoint. As such saturable absorption dye, there are enumerated cyanine-based dye, a phthalocyanine-based dye and naphthalocyanine-based dye. For example, there can be enumerated
dyes produced by EXCITON corporation (U.S.A.) under the trade names of DTTC, HITC, IR-125, IR-140, IR-144 or the like. In particular, naphthalocyanine-based dye should be preferable because it has a large molecular absorption coefficient and a high
optical stability.
According to the present invention, there is provided the optical recording medium in which the recorded pattern recorded on the transparent substrate as concavities and convexities or the change of the optical characteristics relative to the
information signal is detected by the change of reflection of the reproducing light which is perpendicularly introduced from the transparent substrate side and moves to scan the transparent substrate relatively to thereby reproduce a signal. In this
optical recording medium, one layer containing at least the saturable absorption dye is formed on the recording pattern and the molecular absorption coefficient .epsilon. of the saturable absorption coefficient in the wavelength of the reproduced light
is 10.sup.4 or greater. Also, the relaxation time .tau. thereof is set in a range of from 1 ns .ltoreq..tau..ltoreq. 100 ns. Therefore, it is possible to reproduce very small recording patterns smaller than the diffraction limit of the reproduced
light.
Further, according to the structure shown in FIG. 2, there is provided the saturable absorption dye containing layer 2 whose absorptivity is large at normal temperature, i.e., under the state that the reproducing light is not irradiated thereon
and whose portion radiated with a light of constant light amount or more is set in the saturable absorption state to make the absorptivity become zero. Therefore, if a reproducing light is radiated on this optical recording medium, areas in which the
absorptivity of the saturable absorption dye containing layer 2 becomes zero, i.e., a reflected light can be obtained sufficiently are formed in the spot of the reproduced light.
In particular, if the molecular absorption coefficient .epsilon. and the relaxation time .tau. of the saturable absorption dye are selected as described above, even when recording patterns such as a plurality of recording pits or the like are
provided within the beam spot, it is possible to obtain a reflected light by placing only very small areas corresponding to the recording patterns in the saturable state, thus reproduction with super resolution becomes possible.
Accordingly, without modifying a reproducing apparatus with a considerably large modification, such as reducing a wavelength of a reproduced light, using a focusing lens having a large NA (numerical aperture) or changing a signal demodulation
system or the like, information amount about four times as large as the present one can be stored in an optical recording medium of about the same size as that of the present optical recording medium.
As a result of vigorous study and research of the inventor et al. of the present application, it became clear that, particularly in this optical recording medium, if a Fresnel reflection is increased by forming a film having a refractive index
higher (or lower) than those of the substrate 1 and the dye containing layer 2 between the transparent substrate 1 and the saturable absorption dye containing layer 2 and a resonator structure which confines a light is formed within the dye containing
layer 2, then intensity of a reproduced signal can be increased considerably.
A principle thereof will be describe below in brief.
As shown in FIG. 2, by inserting the high refractive index layer or low refractive index layer into a super resolution reproducing disk formed of a substrate/saturable absorption dye containing layer/reflection layer, it is possible to increase
an amount of light which does not travel the saturable absorption dye containing layer but is reflected on the surface thereof and then returned.
FIGS. 3A and 3B show conceptual diagrams of the state at that time. A reflected light RA is a result obtained when a light amplitude AR2 which does not travel back and forth in the saturable absorption dye containing layer 2 but is reflected on
the surface thereof, and a light amplitude AR1 which is returned after it traveled back and forth in the saturable absorption dye containing layer 2 interfere with each other. The light amplitude AR2 doe not pass through the saturable absorption dye
containing layer 2 so that its beam profile becomes exactly the same as that of the incident light. On the other hand, because the light amplitude AR1 traveled back and forth in the saturable absorption dye containing layer 2, the amplitude at the
peripheral portion thereof is relatively lowered as compared with the center of the beam and has therefore a beam profile which is sharpened more.
If these lights have relative amplitude intensities in which the light amplitude AR1 is large at the central portion and the light amplitude AR2 is large at the peripheral portion, then areas in which the light amplitudes AR1 and AR2 become
exactly equal to each other exist in an annular fashion. If the light amplitudes AR1 and AR2 are displaced from each other by a half wavelength, then a reflection intensity of such portion becomes zero due to interference.
Further, if such optical recording medium is formed by sequentially forming the transparent substrate 1, the high (or low) refractive index layer 3, the saturable absorption dye containing layer 2 and the reflection layer 4 whose reflectivity on
the air boundary is 70% or higher, then information can be reproduced from the optical recording medium stably and reliably.
Further, if the real portion refractive index of the above-mentioned high refractive index layer is selected to be 1.8 or greater, then the above-mentioned resonator structure can be formed reliably and therefore intensity of the reproduced
signal can be improved sufficiently.
Furthermore, if the above-mentioned high refractive index layer is made of an inorganic ceramic material formed by the vacuum thin film forming method, then a heat-resisting property can be improved. Also, the manufacturing process thereof can
be simplified and a film forming property thereof can be improved.
In addition, if the mixed film of ZnS and SiO.sub.2 is used as the inorganic ceramic material, when the optical recording medium according to the present invention is applied to a so-called compact disc (CD) in which recording pits are formed by
concavities and convexities, there can be obtained a relatively large reproduced output of 40 dB or greater.
BRIEF DESCRIPTION OF THE DRAWINGS
FIGS. 1A and 1B are schematic diagrams showing structures of optical recording media according to the present invention, respectively;
FIG. 2 is a schematic cross-sectional view showing a main portion of an optical recording medium according to the present invention in an enlarged scale;
FIG. 3A is a cross-sectional view showing reflected lights and a saturable absorption dye containing layer;
FIG. 3B is a schematic diagram showing a distribution of amplitude intensity of reflected lights;
FIG. 4 is a schematic diagram showing a multi-layer system;
FIG. 5 is a diagram showing an example of a calculated distribution of refractive indexes of an optical recording medium and calculated beam profiles of reproducing and reflected light applied to and reflected by the optical recording medium;
FIG. 6 is a diagram showing another example of a calculated distribution of refractive indexes of an optical recording medium and calculated beam profiles of reproducing and reflected light applied to and reflected by the optical recording
medium;
FIG. 7 is a diagram showing still another example of a calculated distribution of refractive indexes of an optical recording medium and calculated beam profiles of reproducing and reflected light applied to and reflected by the optical recording
medium;
FIG. 8 is a graph showing transmittances and reflectivities of saturable absorption dye containing layers used in EXPERIMENTAL EXAMPLE 2 at various film thicknesses thereof;
FIG. 9 is a schematic view of an optical system for measuring the reflectivity of an optical recording medium;
FIG. 10 is a graph showing the relationship between the output of reproducing light and the reflectivity in the position where the reproducing light is focused;
FIG. 11 is a graph showing the reflectivity as it varies when the linear attenuation coefficient of the saturable absorption dye containing layer varies;
FIG. 12 is a graph showing a spectrum of transmittances of a substrate combined with a saturable absorption dye containing layer used in EXPERIMENTAL EXAMPLE 3;
FIG. 13 is a graph showing transmittances and reflectivities of saturable absorption dye containing layers used in EXPERIMENTAL EXAMPLE 3 at various film thicknesses thereof;
FIG. 14 is a diagram showing a reproduced signal from an optical recording medium used in EXPERIMENTAL EXAMPLE 3;
FIG. 15 is a diagram showing a spectrum of transmittances of an optical recording medium according to the present invention;
FIG. 16 is a diagram showing a spectrum of reflectivities of an optical recording medium according to the present invention;
FIG. 17 is a diagram showing a spectrum of reproduced signal outputs from an optical recording medium according to the present invention; and
FIG. 18 is an enlarged fragmentary cross-sectional view of an optical recording medium according to another embodiment of the present invention.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
Specific embodiments to which the present invention is applied will be described hereinafter on the basis of experimental results. Prior to describing the embodiments of the invention, a super resolution achieved by the saturable absorption
phenomenon will be described from a theory standpoint.
More specifically, the saturable absorption phenomenon in the saturable absorption dye containing layer in the optical recording medium in which the saturable absorption dye containing layer and the reflecting layer are sequentially formed on the
transparent substrate was obtained from a simple velocity equation, a transmittance of a reproduced light relative to the reflecting film was calculated to thereby obtain a distribution of a reflectivity of the optical recording medium and a beam profile
of the reflected light under the condition that the reproducing light was moving on the optical recording medium. Initially, the velocity equation of the saturable absorption phenomenon of the saturable absorption dye containing layer will be described
below. Let it be assumed that the saturable absorption dye is set in the excited state from the ground state when it absorbs a light and then returned to the ground state through the relaxation time .tau.. Then, considering the change of a molecularity
G in the ground state at the unit area (cm.sup.-2) , the molecularity G in the ground state is expressed by the following equation (1): ##EQU1## where N is the total molecularity, A is the absorptivity, I is the reproduced light intensity, .lambda. is
the reproduced light wavelength, c is the speed of light, and h is the Planck's constant. Incidentally, it is determined that the saturable dye does not absorb light at all in its excited state.
At that time, the above absorptivity A is determined by a linear attenuation coefficient k (imaginary number component of complex refractive index) of the saturable absorption dye containing layer, the structure and thickness of the film and the
optical constant. Incidentally, the above linear attenuation coefficient k is expressed by the molecularity G, the film thickness d and the molecular absorption constant .epsilon. as in the following equation (2) (in the equation (2), NA represents
Avogadro's number): ##EQU2##
Then, a relationship between the absorptivity A and the linear attenuation coefficient k was obtained by the calculation of the reflectivity of the multilayer film. In the multilayer film system, this relationship was calculated by the equation
provided under the regular reflection condition relative to the multilayer on the basis of the structures, thickness and complex refractive indexes of these films. In the above-mentioned multilayer, if a film thickness of each film is taken as dj and a
complex refractive index of each film is taken as ncj (=nj-ikj), then a reflectivity R, a transmittance T and an absorptivity A are respectively expressed by the following equations (3), (4) and (5):
At that time, all, a12, a21, a22 tj-1, sj and .delta.j are expressed as in the equations (6), (7), (8) and (9). In this case, all, a12, a21 and a2 represent respective components of propagation matrixes of the multilayer film system, tj
represents a transmittance coefficient at the boundary between jth and j+1th layers, sj represents (reflection coefficient/transmittance coefficient) on the same boundary surface and .delta.j represents the phase displacement across a jth layer: ##EQU3##
In this fashion, a relationship between absorptivity and the linear attenuation coefficient k was obtained. If the molecularity of the saturable absorption dye which is in the ground state within the saturable absorption dye containing layer is
changed, then due to a Kramers-Kronig relationship, not only the imaginary part but also the real part of the complex refractive index is changed. In this case, it is considered that the dye is dispersed thinly and therefore the change of the real part
refractive index was neglected in the calculation of that time.
Accordingly, the practical reflectivity distribution of the optical recording medium and the beam practical profile of the reflected light were obtained by using the above-mentioned equations. As the optical recording medium having the high
refractive index layer, there was assumed such one that the transparent substrate 1 made of glass has formed thereon the saturable absorption dye containing layer 2 made of the saturable absorption dye and the binder on which the reflection layer 3 made
by evaporating the aluminum is formed as shown in FIG. 1. The complex refractive indexes of the transparent substrate and the reflection film were assumed to be 1.5-i0 and 1.9-i7, respectively. The thickness of the saturable absorption dye containing
layer was assumed to be such one that the reflectivity becomes zero in the initial state (output of the reproduced light is zero) or that substantially minimizes the reflected light intensity produced by the interference relative to the light intensity
of the reproduced light under the condition that a reproduced light of a small output is irradiated, i.e., such one that the phase of the reflected light from the saturable absorption dye containing layer/transparent substrate boundary surface and the
phase of the saturable absorption dye containing layer/reflection film boundary surface are displaced from each other by 180.degree., i.e., the thickness of the saturable absorption dye containing layer satisfies a s-called non-reflection condition. The
complex refractive index thereof was assumed to be 1.5-i0.3 and the film thickness thereof was assumed to be 180 nm.
FIG. 5 shows calculated results obtained in the above optical recording medium when molecular absorption constant .epsilon. of the saturable absorption dye was assumed to be 5.times.10.sup.5, the relaxation time .tau. was assumed to be 5 ns,
the rotation linear velocity v of the optical recording medium was assumed to be 4 m/s, the spot diameter of the reproduced light was assumed to be 2 .mu.m, the laser light was assumed as the reproduced light, the wavelength of the laser light was
assumed to be 780 nm, and the output power thereof was assumed to be 1 mW, respectively. Although the initial reflectivity of this optical recording medium was 5%, it became clear that, if the above-mentioned reproduced light was irradiated thereon, a
reflectivity shown by a solid line in FIG. 5 was increased to 25% in the center of the beam spot of the reproduced light. Then, it can be understood that the super resolution occurred in which the laser beam diameter at 1/e2 of the peak power was 73% of
the incident light.
In this case, in order to examine the insertion effect of the high refractive index layer, let us consider the case that a film having a refractive index of 1.8-i0 and whose film thickness is 110 nm which is 1/4 wavelength of the reproduced laser
wavelength. FIG. 6 shows calculated results obtained under the similar reproduction conditions. Study of FIG. 6 reveals that, at that time, the reflectivity as increased from 0.5% to 18% at the center of the laser beam. Also, study of FIG. 6 reveals
that stronger super resolution occurred in which the laser beam diameter at 1/e2 of the peak power occupies 63% of the incident light.
Subsequently, in order to examine the insertion effect of a layer with a higher refractive index, let us consider the case that a film having a refractive index of 2.3-i0 and whose film thickness is 85 nm which is 1/4 wavelength of the reproduced
laser wavelength. FIG. 7 shows calculated results obtained under similar conditions (laser power was increased 50%). Study of FIG. 7 reveals that, at that time, the reflectivity was increased from 3.5% to 13% at the center of the laser beam. Also,
study of FIG. 7 reveals that stronger super resolution occurred in which the laser beam diameter at 1/e2 of the peak power occupies 48% of the incident light.
At that time, the beam profile of the reflected laser beam became zero. The reason for this is that the amplitude of the light that traveled back and forth the dye and that of the light reflected on the surface of the dye are equal to each other
with the result that the beam profile becomes zero due to interference.
Incidentally, it is clear that, even when a layer to be inserted is a low refractive index layer, the super resolution becomes strong as the refractive index difference becomes large similarly to the case that the high refractive index layer is
inserted. Therefore, specific simulated numerical values need not be described.
EXPERIMENTAL EXAMPLE 1
In this experimental example, an optical recording medium was manufactured in actual practice, and how the reflectivity was changed when a reproducing light was radiated on the optical recording medium was investigated.
Initially, a complex refractive index of the saturable absorption dye containing layer was measured. Bis (tri-n-hexylsiloxy) silicon naphthalocyanine (hereinafter simply referred to as SINC) was used as a saturable absorption dye, and a
polymethylacrylate (hereinafter simply referred to as PMMA) having a molecular weight of 400000 was used as a binder. The SINC and the PMMA were dissolved into chloroform and coated on a glass substrate serving as a transparent substrate by a spin
coating method. Then, saturable absorption dye containing layers while the film thicknesses thereof were being changed in a range of from 100 to 200 nm. A mixing ratio of the SINC, the PMMA and chloroform was 2:15:500. When these were mixed, PMMA was
perfectly dissolved by stirring and heating for several hours and SINC also was perfectly dissolved by stirring with an ultrasonic cleaner. Chemical structures of SINC and PMMA are shown by the following chemical formulas (1) and (2): ##STR1##
Transmittances and reflectivities of the saturable absorption dye containing layers thus obtained were measured, and measured results are illustrated in FIG. 8. In FIG. 8, an open circle represents a measured transmittance of the saturable
absorption dye containing layer having a thickness of 170 nm, and a solid circle represents a measured reflectivity. In FIG. 8, a dashed line and a solid line represent measured transmittance and reflectivity of the optical recording medium having he
complex refractive index of 1.7-i0.3 . Study of FIG. 8 reveals that the measured results shown by the open circle and the solid circle and the transmittance and the reflectivity of the optical recording medium having the complex refractive index of
1.7-i0-.3 shown by the solid and dashed lines are well coincident. Thus, it can be judged that a complex refractive index of the measured saturable absorption dye containing layer is 1.7-i0.3.
Subsequently, an optical recording medium was manufactured by using a transparent substrate in which a film thickness of the saturable absorption dye containing layer was 170 nm. More specifically, a reflection film formed of an aluminum
evaporation film was formed on the saturable absorption dye containing layer formed on the transparent substrate. In that case, as an evaporating apparatus, there was used such one that was manufactured by NICHIDEN ANERVA CORP. under the trade name of
EVD-500A. Then, the evaporation was carried out by an ordinary method under the condition that a vacuum degree was 3.times.10.sup.-4 Pa and an evaporation rate was about 2 nm/s. A film thickness was selected to be 400 nm and this film thickness was
measured and confirmed by a film thickness meter based on quartz oscillation.
Then, a reflectivity of the above-mentioned optical recording medium was measured by an optical system shown in FIG. 9. As shown in FIG. 9, this optical system is comprised of a semiconductor laser (LD) 14 serving as a reproducing light source,
a polarizing beam splitter (PBS) 13 for splitting a reproducing light and a reflected light, a quarter wave plate (Qup) 12, and a focusing lens 11. A reproducing light, which is shown by an arrow L in FIG. 9, is emitted from the semiconductor laser (LD)
14 and traveled through the polarizing beam splitter (PBS) 13, the quarter wave plate (Qup) 12 and the focusing lens 11 to radiate an optical recording medium 10. The reproducing light that was radiated on the optical recording medium 10 travels through
the focusing leans 11 and the quarter wave plate (Qup) 12 as a reflected light shown by an arrow R in FIG. 9 and splitted by the reproducing light L with the polarizing beam splitter (PBS) 13, thereby being detected. The optical recording medium 10 is
set on a rotating disk, not shown, and can be rotated. Then, a reflectivity was measured under the condition that a rotational linear velocity of the optical recording medium 10 was selected to be 1.5 to 4.5 m/s, the wavelength of the reproducing light
was selected to be 780 nm which falls in a laser wavelength region, an output power of the reproducing light required when the reproducing light radiates the optical recording medium 10 was selected in a range of from 1 to 10 mW and that an NA of the
focusing lens 11 was selected to be 0.4.
As a result, it was observed that a reflected light intensity on the optical recording medium 10 at its extremely small portion which corresponds to the focused position of the reproducing light is increased as the output power of the reproducing
light is increased. In that case, it was confirmed that the reflectivity was increased while the intensity of the reproducing light was not changed.
FIG. 10 shows measured results of the output power of the reproducing light and the change of the reflectivity at the focused position of the reproducing light. It was confirmed from measured results of FIG. 10 that the reflectivity was changed
with the change of the output level of the reproducing light. Also, as the output level of the reproducing light is changed in a range of from 0 to 10 mW, the reflectivity is changed from 10% to 20%. This seems to be achieved by the saturable
absorption effect of the saturable absorption dye containing layer.
FIG. 11 shows measured results of the change of reflectivity obtained when the linear attenuation coefficient of the saturable absorption dye containing layer of the optical recording medium was changed. In the optical recording medium according
to this experimental example, it was confirmed that the linear attenuation coefficient k of the saturable absorption dye containing layer was 0.3. Study of measured results of FIG. 11 reveals that the reflectivity was improved from 10% to 20% because
the linear attenuation coefficient k was lowered to 0.2 with the radiation of the reproducing light. Therefore, it is concluded that the change of the reflectivity in the above optical recording medium was caus | | |