| United States Patent | 5525281 |
| Link to this page | http://www.wikipatents.com/5525281.html |
| Inventor(s) | Lorcks; Jurgen (Rees, DE);
Pommeranz; Winfried (Enger, DE);
Heuer; Joachim (Kranenburg, DE);
Klenke; Kurt (Kleve, DE);
Schmidt; Harald (Emmerich, DE) |
| Abstract | There is provided a method for preparing biodegradable films from
plant-based raw materials in the form of carbohydrates which method is
continuous and carried out in one step. In the process the plant-based raw
materials are modified and plastified and the films are prepared without
interruption and in one step. The advantages of the invention reside in
reduced shear stress of the starch molecules and thus in the improved
properties of the films as well as in the cost-efficient, time-, energy-
and space-saving manufacture. |
|
|
 |
Title Information  |
|
|
|
|
|
Drawing from US Patent 5525281 |
|
|
Method for preparing biodegradable films from plant-based raw materials |
|
|
|
|
|
| Publication Date |
June 11, 1996 |
|
|
|
|
|
| Filing Date |
March 15, 1995 |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Priority Data |
Aug 24, 1992[DE]42 28 016.8 |
|
|
|
|
|
|
|
|
 |
|
 |
Title Information |
|
|
|
References |
|
|
| *references marked with an asterisk below are user-added references |
 |
U.S. References |
|
|
|
 |
|
|
|
U.S. References |
|
|
|
Foreign References |
|
|
|
|
|
|
|
|
Foreign References |
|
|
|
Other References |
|
|
|
|
|
|
|
|
Other References |
|
|
|
|
|
|
|
References |
|
|
|
|
|
|
| Market Size |
|
Estimate the gross annual revenues of the relevant market
sector:
|
| | |
| |
|
|
| Market Share |
|
Estimate the percentage of the relevant market sector this invention will capture:
|
| | |
| |
|
|
| Reasonable Royalty |
|
What percentage of gross sales should the inventor or assignee be paid?
|
| | |
| |
|
|
|
Public's "Guesstimation" of Royalty Value
|
| Market Size | N/A | [No votes] | | x | Market Share | N/A | [No votes] | | x | Reasonable Royalty | N/A | [No votes] |
| | N/A | |
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Market Review |
|
|
|
Technical Review |
|
|
|
Claims |
|
|
We claim:
1. A method for preparing biodegradable films from plant-based raw
materials, preferably in the form of carbohydrates by means of a
screw-type extruder, wherein modification or disintegration and the
plastification of the plant-based raw materials and subsequent film
preparation are done continuously and in one step comprising the stages
of:
a. continuously adding measured plant-based raw materials and, if desired,
solid additives through a first inlet (11) as well as, if desired, liquid
additives through a second inlet (12) in a first extruder section (1) and
mixing them to form a mixture,
b. heating and kneading the mixture in a second extruder section (2),
c. heating and reacting the mixture in a third extruder section (3) to form
a melt,
d. evacuating said melt in a vacuum apparatus (14) in a fourth extruder
section (4) by extracting and allowing water to evaporate from the melt,
thus causing the melt to cool down,
e. further cooling the melt in a fifth extruder section (5),
f. compressing the melt in a sixth extruder section (6),
g. extruding the melt from the extruder through a die (7, 8, 9) to form a
film (15, 16).
2. A method as defined in claim 1 wherein in stage b. liquid additives are
added through a third inlet (13).
3. A method as defined in claim 1 wherein the plant-based raw materials is
selected from the group consisting of flour or native starch in natural or
hybrid form derived from potatoes, manioc, peas, beans, corn, wax corn,
corn with high amylose content, grain selected from wheat and fractions
prepared therefrom, barley or sorghum, starch derivatives consisting of
physically or chemically modified starch, cellulose derivatives, plant
rubber, hemicellulose, polysaccharides, hydrocolloids or mixtures of one
or more of those raw materials.
4. A method as defined in claim 1 wherein the temperature is selectively
adjustable in the first to sixth sections (1 to 6).
5. A method as defined in claim 1 wherein the die is a tubular die (7) and
a blown film (15) is molded.
6. A method as defined in claim 1 wherein the die is a double tubular die
(8) and a blown film (15) is molded.
7. A method as defined in claim 1 wherein the die is a flat slot die (9)
and a flat film (16) is molded.
8. A method as defined in claim 1 wherein a metering device (17) for the
plant-based raw materials and additives is provided in front of the first
inlet (11).
9. A method as defined claim 1 wherein a gear pump (18) or at least one
one-lead screw (19) is provided between the screw-type extruder (10) and
the die (7, 8, 9).
10. A method as defined in claim 1 wherein the screw-type extruder (10) is
a two-shaft screw-type extruder.
11. A method as defined in claim 10 wherein the two-shaft screw-type
extruder (10) has the following configuration:
a. right-handed with a first slope in the first and second sections (1 and
2, respectively),
b. right- and left-handed with the first slope in the third section (3)
while alternating one or several times.
c. steeply right-handed with a second slope in the fourth and fifth
sections (4 and 5, respectively), and
d. flatly right-handed with a third slope in the sixth section (6), wherein
the second and the third slopes are greater and smaller, respectively,
than the first slope.
12. A method as defined in claim 4 wherein the following temperature
conditions are adhered to: 10.degree. to 80.degree. C., preferably
50.degree. C., in the first section (1); 10.degree. to 150.degree. C.,
preferably 80.degree. to 100.degree. C., in the second section (2);
70.degree. to 200.degree. C., preferably 120.degree. to 160.degree. C., in
the third section (3); 70.degree. to 200.degree. C., preferably
120.degree. to 160.degree. C., in the fourth section (4); 70.degree. to
200.degree. C., preferably 80.degree. to 120.degree. C., in the fifth
section (5); 40.degree. to 200.degree. C., preferably 40.degree. to
60.degree. C., in the sixth section (6); 40.degree. to 150.degree. C.,
preferably 50.degree. to 70.degree. C., at the die (7; 8; 9).
13. A method as defined in claim 1 wherein the films in the dry state
contain 40 to 100% by wt., preferably 75 to 95% by wt., of carbohydrates.
14. A method as defined in claim 1 wherein glycerol-monostearate is added
as an additive preferably in the first section (1) to act as an
emulsifier.
15. A method as defined in claim 1 wherein glycerol is added as an additive
preferably in the second section (2) to act as a plastifier.
16. A method as defined in claim 1 wherein water is added as an additive
preferably in the second section (2) to act as a solvent.
17. A method as defined in claim 4 wherein potassium sorbate is added as an
additive preferably in the first section (1) to act as a preservative.
18. A method as defined in claim 1 wherein the films (15; 16) in the dry
state contain 0 to 25% by wt., preferably 0.1 to 2.5% by wt., of glycerol
monostearate, 0 to 40% by wt., preferably 10 to 28% by wt., of glycerol;
and 0 to 5% by wt., preferably 0.1 to 0.5% by wt., of potassium sorbate.
19. A method as defined in claim 1 wherein the films (15; 16) contain 0 to
35% by wt., preferably 10 to 20% by wt., of water.
20. Films from plant-based raw materials producible by the method as
defined in claim 1. |
|
|
|
|
|
|
Claims |
|
|
|
Description |
|
|
FIELD OF THE INVENTION
The invention relates to a method for preparing biodegradable films from
plant-based raw materials. Such methods are gaining more and more
importance, for example, in the production of environmentally compatible
packing material. The object is to produce films having sufficient
strength that can easily be disintegrated or dissolved into their original
natural components.
BACKGROUND OF THE INVENTION
Methods for preparing thermoplastic granules by using starches have been
disclosed previously (U.S. Pat. Nos. 4,133,784, 4,021,388, DE-A-23 22
440). Such granules are processed to films in a second procedural step. In
so doing, the starch is used as filler material in synthetic polymers.
Furthermore, methods for preparing and modifying destructured
thermoplastic starch have been disclosed (EP-A-378 646, EP-A-397 819).
WO 90/05161 A1 shows thermoplastically processable starch as well as a
method for preparing it. In the process aggregates and, if desired,
various further additives are added to raw starch material to reduce the
melting temperature of the starch to a level below its decomposition
temperature. This is to improve the structure of the starch melt so as to
facilitate handling in preparing and processing thermoplastic starch.
EP-A1-0 474 095 discloses a process of preparing biodegradable articles,
such as dishes, cups, cardboard boxes, etc. using plant-based raw
material, such as starch, as starting material. This material is
supplemented with additives, plastified and converted in a first extruder
to an intermediate to form a billet or granules. Then the intermediate is
molded in a second extruder into the desired article.
Similarly, conventional film preparation from plant-based raw materials
proceeds in two completely separate steps. The biopolymer melt
destructured and plastified in the extrusion process is cooled at the end
of the first step, forced through a die under high pressure and
granulated. In order to avoid biopolymer foaming, it is required to cool
the melt. The resulting high shear stress causes damage to the molecular
structure of the starch while various molecule fragments are split off.
The polymer chains of the starch are shortened and the molecular weight is
reduced. The obtained starch granules are then processed to films in a
further extrusion process subject to similar conditions. In the process
the biopolymer is again decomposed as the molecular weight is reduced and
the chains are shortened. The two-fold damage to the molecular structure,
especially the shortening of the amylose chains, causes immediate
deterioration of the properties (tensile strength, elasticity, etc.) of
the thus obtained films. What is more, the two-fold extrusion is time-,
energy- and cost-consuming.
By contrast, the object underlying the present invention is to provide a
cost-efficient method for preparing biodegradable films from plant-based
raw materials while avoiding the drawbacks of the prior art, improving the
quality of the obtained films and achieving, for instance, high tensile
strength and elasticity.
This object is achieved by providing the features indicated in the claims.
SUMMARY OF THE INVENTION
In achieving the object, the invention is based on the concept of
optionally disintegrating and modifying plant-based raw materials, e.g.,
in the form of carbohydrates, in a continuous and one-step process without
involving intermediates and without interruption, of plastifying as well
as of compressing and molding them into films. A suitable configuration of
a screw-type extruder to transport the film materials and suitable
temperature conditions ensure careful processing of the biopolymers.
The plant-based raw materials can include carbohydrates, e.g., flour or
native starch in natural or hybrid form-derived, for example, from
potatoes, manioc, peas, beans, corn, wax corn, corn with high amylose
content, grain such as wheat and fractions prepared therefrom, barley or
sorghum, starch derivatives consisting of physically and/or chemically
modified starch, cellulose derivatives, plant rubber (carbohydrate
polymer), hemicellulose, polysaccharides, hydrocolloids or mixtures of one
or more of those raw materials.
The invention has the following advantages.
The method of the invention reduces the shear strength, fragmentation and
molecular weight loss of the biopolymers. As a result, the preparation
process is considerably facilitated because the reaction extruder and the
film preparation form a process unit. The storage of hygroscopic pellets
in an aluminum compound under vacuum is no longer necessary. Compounding
and film preparation occur in one step. The production is more
cost-efficient as no packing and transportation of the pellets are
required and as less personnel and equipment costs are incurred. In
addition, energy for transporting and melting the pellets can be saved.
The obtained films exhibit improved properties in comparison to the prior
art.
BRIEF DESCRIPTION OF THE DRAWINGS
The invention is further illustrated below by means of drawings.
FIG. 1a shows a lateral view of a production line of the invention for the
production of blown films.
FIG. 1b shows a top view of a production line of the invention as shown in
FIG. 1a.
FIG. 2a shows a lateral view of a production line of the invention for the
production of flat films.
FIG. 2b shows a top view of a production line of the invention as shown in
FIG. 2a.
FIG. 3a shows an embodiment of the invention featuring the end of a
screw-type extruder comprising a double tubular die.
FIG. 3b shows an embodiment of the invention featuring the end of a
screw-type extruder comprising a tubular die.
FIG. 3c shows an embodiment of the invention featuring the end of a
screw-type extruder comprising a flat die.
DETAILED DESCRIPTION OF THE INVENTION
FIGS. 1a and 1b show a production line of the invention for the production
of blown films in two views. Depicted are individual production sections 1
to 6 and a die 7 interconnected by a screw-type extruder (not shown) that
transports and mixes or kneads the film materials. A mixture of solid
plant-based raw materials and, if desired, additives is measured with a
metering device 17 (only shown in FIG. 1a) and added via the first inlet
11 of the first section 1. At the same time, liquid additives can be added
via the second inlet 12. Examples of additives include emulsifiers,
plastifiers, preservatives and water. In section 2 the mixture is heated
and kneaded. Liquid additives can be added via a third inlet 13. In a
third section 3 the temperature is further increased and the plant-based
raw materials are allowed to react with the additives, thus forming a
melt. In a fourth section 4 the melt is evacuated in a vacuum apparatus 14
by allowing water to evaporate from the melt and thus causing the melt to
cool down. The melt is further cooled in a fifth section 5. In a sixth
section 6 the melt is compressed so as to cause a pressure built-up in the
die and then blown through a tubular die 7 to form a film 15. A similar
production line is depicted in FIGS. 2a and 2b (metering device 17 is only
shown in FIG. 2a). The difference between FIGS. 2a, 2b and FIGS. 1a, 1b
lies in the fact that a flat film 16 is molded by a flat die 9.
FIG. 3a shows an embodiment of the invention wherein a blown film 15 is
produced by means of a double tubular die 8. Two one-lead screws 19 are
provided behind a double-lead screw 10 to transport the melt to the die 8.
In FIG. 3b a blown film 15 is produced by means of a tubular die 7. The die
is supplied with the melt by a gear pump 18 provided behind the
double-lead screw 10.
In an embodiment comprising a flat die 9 for the production of a flat film
16 as shown in FIG. 3c the double-lead screw 10 feeds the melt directly to
the die 9.
The screw-type extruder 10 is preferably shaped like a double-lead screw
and preferably has the following configurations in each of sections 1 to
6: right-handed in sections 1 and 2; right- and left-handed in section 3
while optionally alternating several times; steeply right-handed in
sections 4 and 5; and flatly right-handed in section 6. These differing
configurations ensure controlled and differing transport rates, kneading
and mixing in each of the sections and thus the desired careful handling
of the biopolymers.
Sections 1 to 6 and dies 7, 8 or 9 exhibit a controlled temperature
distribution. Preferred temperature conditions include: 50.degree. C. in
section 1; 80.degree.-100.degree. C. in section 2; 120.degree.-160.degree.
C. in section 3; 120.degree.-160.degree. C. in section 4; 80.degree. to
120.degree. C. in section 5; 40.degree.-60.degree. C. in section 6; and
50.degree. to 70.degree. C. at dies 7, 8 or 9.
The embodiments of the method of the invention are shown below. A two-shaft
screw-type extruder (ZSK 40) manufactured by Werner und Pfleiderer,
Germany, was used.
EXAMPLE 1
A solids mixture comprising potato starch and an emulsifier
(mono-diglyceride) as well as the liquid components water and glycerol
were continuously added to the two-shaft screw-type extruder.
______________________________________
Solids:
Potato starch 99%
Emulsifier 1%
100%
Liquid additives:
Water 14%
Glycerol 86%
100%
Mixing ratio during the process:
Solids 75%
Liquids 25%
Temperature profile:
Section 1: 50.degree.
C.
Section 2: 80.degree.
C.
Section 3: 120.degree.
C.
Section 4: 120.degree.
C.
Section 5: 80.degree.
C.
Section 6: 60.degree.
C.
Die: 60.degree.
C.
RPM: 170 min.sup.-1
Torque: 30%
Pressure: 80 bar
Blow ratio: 1:4
______________________________________
A transparent film having the following properties was obtained:
______________________________________
Film thickness: 35 .mu.m
Tensile strength along length:
12.1 N/mm.sup.2
Tensile strength along width:
11.8 N/mm.sup.2
Duration of dissolution of 10 g of film
15 minutes
in 100 g of water at 20.degree. C.:
______________________________________
EXAMPLE 2
A solids mixture comprising potato starch and an emulsifier
(mono-diglyceride) as well as the liquid components water and glycerol
were continuously added to the two-shaft screw-type extruder.
______________________________________
Solids:
Potato starch 99%
Emulsifier 1%
100%
Liquid additives:
Water 20%
Glycerol 80%
100%
Mixing ratio during the process:
Solids 75%
Liquids 25%
Temperature profile:
Section 1: 50.degree.
C.
Section 2: 80.degree.
C.
Section 3: 140.degree.
C.
Section 4: 140.degree.
C.
Section 5: 100.degree.
C.
Section 6: 60.degree.
C.
Die: 60.degree.
C.
RPM: 170 min.sup.-1
Torque: 20%
Pressure: 60 bar
Blow ratio: 1:4
______________________________________
A transparent film having the following properties was obtained:
______________________________________
Film thickness: 30 .mu.m
Tensile strength along length:
10.2 N/mm.sup.2
Tensile strength along width:
9.4 N/mm.sup.2
Duration of dissolution of 10 g of film
11 minutes
in 100 g of water at 20.degree. C.:
______________________________________
EXAMPLE 3
A solids mixture comprising potato starch and an emulsifier
(mono-diglyceride) as well as the liquid components water and glycerol
were continuously added to the two-shaft screw-type extruder.
______________________________________
Solids:
Potato starch 99%
Emulsifier 1%
100%
Liquid additives:
Water 10%
Glycerol 90%
100%
Mixing ratio during the process:
Solids 75%
Liquids 25%
Temperature profile:
Section 1: 50.degree.
C.
Section 2: 80.degree.
C.
Section 3: 160.degree.
C.
Section 4: 160.degree.
C.
Section 5: 120.degree.
C.
Section 6: 60.degree.
C.
Die: 60.degree.
C.
RPM: 230 min.sup.-1
Torque: 15%
Pressure: 52 bar
Blow ratio: 1:4
______________________________________
A transparent film having the following properties was obtained:
______________________________________
Film thickness: 33 .mu.m
Tensile strength along length:
9.4 N/mm.sup.2
Tensile strength along width:
8.2 N/mm.sup.2
Duration of dissolution of 10 g of film
8 minutes
in 100 g of water at 20.degree. C.:
______________________________________
EXAMPLE 4
A solids mixture comprising corn starch and an emulsifier
(mono-diglyceride) as well as the liquid components water and glycerol
were continuously added to the two-shaft screw-type extruder.
______________________________________
Solids:
Corn starch 98%
Emulsifier 2%
100%
Liquid additives:
Water 14%
Glycerol 86%
100%
Mixing ratio during the process:
Solids 70%
Liquids 30%
Temperature profile:
Section 1: 50.degree.
C.
Section 2: 80.degree.
C.
Section 3: 140.degree.
C.
Section 4: 140.degree.
C.
Section 5: 100.degree.
C.
Section 6: 60.degree.
C.
Die: 60.degree.
C.
RPM: 200 min.sup.-1
Torque: 18%
Pressure: 45 bar
Blow ratio: 1:3
______________________________________
An opaque film having the following properties was obtained:
______________________________________
Film thickness: 42 .mu.m
Tensile strength along length:
8.2 N/mm.sup.2
Tensile strength along width:
6.8 N/mm.sup.2
Duration of dissolution of 10 g of film
24 minutes
in 100 g of water at 20.degree. C.:
______________________________________
EXAMPLE 5
A solids mixture comprising wheat flour and an emulsifier
(mono-diglyceride) as well as the liquid components water and glycerol
were continuously added to the two-shaft screw-type extruder.
______________________________________
Solids:
Type 405 wheat flour 98%
Emulsifier 2%
100%
Liquid additives:
Water 25%
Glycerol 75%
100%
Mixing ratio during the process:
Solids 70%
Liquids 30%
Temperature profile:
Section 1: 50.degree.
C.
Section 2: 80.degree.
C.
Section 3: 140.degree.
C.
Section 4: 140.degree.
C.
Section 5: 100.degree.
C.
Section 6: 60.degree.
C.
Die: 60.degree.
C.
RPM: 200 min.sup.-1
Torque: 20%
Pressure: 55 bar
______________________________________
The material was molded by a flat slot die and drawn out to a film.
An opaque film having the following properties was obtained:
______________________________________
Film thickness: 94 .mu.m
Tensile strength along length:
9.6 N/mm.sup.2
Tensile strength along width:
9.0 N/mm.sup.2
Duration of dissolution of 10 g of film
64 minutes
in 100 g of water at 20.degree. C.:
______________________________________
EXAMPLE 6
A solids mixture comprising potato starch and an emulsifier
(mono-diglyceride) as well as the liquid components water and glycerol
were continuously added to the two-shaft screw-type extruder. At the end
of the two-shaft section the material was fed to a tubular die via a gear
pump.
______________________________________
Solids:
Potato starch 99%
Emulsifier 1%
100%
Liquid additives:
Water 14%
Glycerol 86%
100%
Mixing ratio during the process:
Solids 80%
Liquids 20%
Temperature profile:
Section 1: 50.degree.
C.
Section 2: 100.degree.
C.
Section 3: 140.degree.
C.
Section 4: 140.degree.
C.
Section 5: 80.degree.
C.
Section 6: 40.degree.
C.
Die: 50.degree.
C.
RPM: 200 min.sup.-1
Torque: 62%
Pressure at pump inlet:
80 bar
Pressure at pump outlet:
210 bar
Blow ratio: 1:4
______________________________________
A transparent film having the following properties was obtained:
______________________________________
Film thickness: 29 .mu.m
Tensile strength along length:
14.1 N/mm.sup.2
Tensile strength along width:
12.6 N/mm.sup.2
Duration of dissolution of 10 g of film
10 minutes
in 100 g of water at 20.degree. C.:
______________________________________
EXAMPLE 7
A solids mixture comprising potato starch and an emulsifier
(mono-diglyceride) as well as the liquid components water and glycerol
were continuously added to the two-shaft screw-type extruder. At the end
of the two-shaft section the material was passed on to two one-lead screws
and from there on fed to a double tubular die 8. In the screws two
concentric tubes were formed from the two product flows, the thus obtained
tubes were immediately laminated one on top of the other and together
blown to a film.
______________________________________
Solids:
Potato starch 99%
Emulsifier 1%
100%
Liquid additives:
Water 20%
Glycerol 80%
100%
Mixing ratio during the process:
Solids 75%
Liquids 25%
Temperature profile:
Section 1: 50.degree.
C.
Section 2: 100.degree.
C.
Section 3: 120.degree.
C.
Section 4: 120.degree.
C.
Section 5: 80.degree.
C.
Section 6: 60.degree.
C.
Die: 70.degree.
C.
RPM: 160 min.sup.-1
Torque: 44%
Pressure: 50 bar
Blow ratio: 1:4
______________________________________
A transparent film having the following properties was obtained:
______________________________________
Film thickness: 38 .mu.m
Tensile strength along length:
11.4 N/mm.sup.2
Tensile strength along width:
9.4 N/mm.sup.2
Duration of dissolution of 10 g of film
31 minutes
in 100 g of water at 20.degree. C.:
______________________________________
* * * * *
|
|
|
|
|
|
|
Description |
|
|
|
|
|