The present invention relates to a product, in particular a panel, that can be obtained by the Hatschek process and without autoclaving, and can be used as siding, cladding element or partition element, this product being formed from a fibre-reinforced cementitious matrix comprising at least one hydraulic binder, such as cement, at least one filler, such as calcium carbonate, and at least synthetic fibres. The invention also relates to a process for manufacturing the product.

Disclosed are concrete and fiber cement formulations and products comprising low-density calcium silicate hydrate, and methods for producing these formulations and products. The disclosed formulations exhibit accelerated curing times. Other advantages of the disclosed formulations include improved dimensional stability in extruded products, reduced cracking, and reduced wash-out in underwater applications. The products of the disclosed formulation have lower cost of production and faster time to market.

A composite product comprising a substrate layer and one or more functional layers applied thereto. The slurry is applied to the substrate layer to form a functional layer and the functional layer dewatered through the substrate layer. The functional layers can be repeated to build up a laminated composite product. Functional additives may be included in each layer to provide desired properties to that layer and indeed to the subsequent composite product.

A fiber-reinforced building material in one embodiment incorporates cellulose fibers that are chemically treated with a dispersant to impart improved dispersibility to the fibers. The fibers are treated with a dispersant which deactivates the hydroxyl sites of the fiber surfaces and in some cases, making the fiber surface more hydrophobic. The dispersant inhibits the hydroxyl groups on the cellulose fiber surface from bonding with hydroxyl groups of other fibers and from bonding with hydroxyl groups of the same fiber, thereby significantly reducing inter-fiber and intra-fiber hydrogen bonding. The treated fibers can be readily dispersed and uniformly distributed throughout a mixture without re-clustering or reclumping once the mechanical mixing action stops. The chemically treated fibers with improved dispersibility improve the fiber distribution and reinforcing efficiency, which in turn improves key physical and mechanical properties of the material such as the modulus of rupture, z-direction tensile strength, and toughness, and surface finishes. With improved fiber reinforcing efficiency, less dosage of fiber is needed to achieve the required physical and mechanical properties.

The present invention provides exterior building products, such as roofing and siding, shake, shingles, siding, sheathing, panels, planks, vertical siding, soffit panels, fencing, decking, fascia, corner posts, column corners and trim boards in which a plurality of cementitious layers are provided with an improved interlaminar bond by employing a resinous bond promoter, a rheological agent, mechanical means to distribute fibers in a direction which is perpendicular to the machine direction so as to bridge between layers in the product, or a combination thereof. These techniques help to increase interlaminar bond strength to improve the mechanical properties of the product. When certain resinous bond promoters are used, the additional benefits of water absorption resistance and pigmentation throughout the product can be provided with minimal expense. Improvements in interlaminar bond strength of about 10 46% were observed with a percent elongation improvement of about 7%.