The present invention provides a novel method to produce grade road base material using recycled oilfield waste, called "oil and gas waste," more specifically, drilling waste and aggregate and a novel road base material. Hydration and mixing of the waste materials along with a binder, will achieve an irreversible pozzolanic chemical reaction necessary for stabilization into a road base. An asphalt emulsifier may be included in the binder to manufacture asphalt stabilized road base. The entire me...

A nonionic water-soluble cellulose ether is characterized in that when 3 pbw of the nonionic water-soluble cellulose ether is added to a mixture of 90 pbw of cordierite, 10 pbw of ordinary Portland cement, and 33 pbw of water, immediately followed by kneading at 20.degree. C. and 20 rpm, a maximum torque for kneading is reached within 180 seconds from the addition. It is suitable as an admixture for extrudable hydraulic compositions. The hydraulic composition to which the inventive admixture is ...

A fast-setting, bioresorbable calcium phosphate cement is prepared by a process which can be carried out with a heat treatment up to 1000.degree. C. on a mixture of a wetting solution and a calcium phosphate powder having a Ca to P molar ratio of 0.5 2.5. The wetting solution suitable for use in the process of the present invention includes water, an organic solvent, an acidic and basic solution. A setting solution for mixing with the heated powder to form the fast-setting, bioresorbable calcium...

Superconducting ceramics having relatively high critical temperatures are composed of rare earth metals, alkaline earth metals and copper. They have few defects and a limited polycrystalline interfacial area.

The invention relates to a process for the production of ceramic bearing components in which a mixture of a metallo-organic compound and a chemically reactive filling substance is subjected to a pyrolysis reaction and the resulting product.

A sintered object of silicon monoxide for use as a material for forming silicon oxide thin films is provided of which the evaporation residue as determined by subjecting a sample thereof to thermogravimetry at a heating temperature of 1,300.degree. C. and in a vacuum atmosphere, namely at a pressure of not higher than 10 Pa, is not more than 4% by mass relative to the sample before measurement. This sintered object can be produced by sintering SiO particles having a particle diameter of not smal...

A method of production of a reduction resistant dielectric ceramic composition having a superior low frequency dielectric characteristic and further improved in accelerated lifetime of insulation resistance, specifically a method of production of a dielectric ceramic composition containing a main component including a dielectric oxide of a specific composition, a first subcomponent including a V oxide, a second subcomponent containing an Al oxide, a third subcomponent containing an Mn oxide, and...

A production method of a dielectric ceramic composition having a step of firing dielectric material including a main component ingredient and a subcomponent ingredient, wherein said main component ingredient before firing is barium titanate ingredient powder having the perovskite type crystal structure expressed by ABO.sub.3, and a ingredient powder having a ratio A/B of A site components and B site components of 1.006.ltoreq.A/B.ltoreq.1.035 and the specific surface area of 8 to 50 m.sup.2/g is...

This invention relates to a piezoelectric ceramic of the formula Pb.sub.(1-z)M.sub.z(Mg.sub.1/3Nb.sub.2/3).sub.x(Zr.sub.yTi.sub.1-y).sub.1- -xO.sub.3 where M can be either Sr or Ba or both and x is in between about 0.1 and about 0.7, y is between about 0.2 and about 0.7, and z is between about 0.02 and about 0.1 and to method for preparing the piezoelectric ceramic. The piezoelectric ceramic is provided as a composite perovskite structure. Additional materials or dopants can be added to the piez...

A method for manufacturing multilayer ceramic electronic components includes the steps of removing organic materials from multilayer ceramic bodies having internal electrodes and ceramic layers, and then sintering the multilayer ceramic bodies. After finishing the removing step, it is preferable that the amount of the remaining organic materials in the multilayer ceramic body is 0.5 to 8.5 weight %, more preferably 1.0 to 5.0 weight %. The removing process may be performed in a neutral, a reduct...