By providing an abrasive having a ratio of volume-cumulative (95%) average particle size (D95) to volume-cumulative (50%) average particle size (D50) (D95/D50) falling within a range of 1.2 to 3.0 or an abrasive having a volume-cumulative (95%) average particle size (D95) falling within a range of 0.1-1.5 .mu.m and containing coarse particles having a size more than 10 times the volume-cumulative (50%) average particle size (D50) in an amount, based on the total mass of all the particles, of 1 m...

An initial solids mixture for a later organic coating, such as pigmented coatings, films, priming coats, etc., e.g., for a coil coating method in which an initial solids mixture is applied to a substrate, e.g., broad strip, and this is thereby pre-coated, wherein the initial solids mixture includes, as additive particles, boron carbide and/or silicon carbide and/or compounds of transition elements or lanthanides, the electrical conductivity of which is selected to be in the metallic range (.sigm...

Silica-calcium carbonate composition particles having the characteristics of both synthetic silica and calcium carbonate are described along with paper having the particles internally filled therein and a method for making the particles.In the carbonation reaction, which typically involves a step of forming calcium carbonate, while agitating a calcium hydroxide slurry, a mixed gas of carbon dioxide and air is introduced thereinto and synthetic silica, such as colloidal silica or the like, is add...

The present invention provides a carbon black for coloring cement excelling in dispersibility in cement slurry, exhibiting superior adhesion to a cement matrix, and excelling in coloring characteristics and strength, and a method for coloring a cement-formed product using the carbon black. The carbon black for coloring cement is a carbon black in which humic acids are adsorbed on the surface by a surface treatment using an aqueous solution in which the humic acids are dissolved. The carbon black...

The present invention relates to a method of producing solid carbonaceous C.sub.xH.sub.y, wherein the ratio of x:y is greater than 2.5:1, or a hydrogen-rich gas, wherein a hydrocarbon fuel is heated with limiting amounts of oxidizer to a temperature of at least about 1000.degree. C. whereby to effect incomplete combustion and pyrolytic decomposition of said hydrocarbon fuel, the carbonaceous product produced by that method, a method of combusting the gas produced by that method and reactors for ...

The invention relates to multilayered luster pigments based on metallic substrates, which are completely surrounded by a plurality of layers, where these layers comprise at least one layer pack (A) having a colorless dielectric layer of a material with a refractive index n of .ltoreq.1.8, and a colorless dielectric layer of a material with a refractive index n of >1.8, and a selectively or non-selectively absorbent layer (B), and to a process for their production, and to their use.

A silicon-titanium mixed oxide powder contains aggregates of primary particles selected from amorphous silicon dioxide particles, crystalline titanium dioxide particles, and silicon-titanium mixed oxide particles each having an amorphous silicon dioxide fraction and a crystalline titanium dioxide fraction. The silicon-titanium mixed oxide particles predominate in the powder. The powder exhibits a BET surface area of from 20 to 200 m.sup.2/g, and a titanium dioxide content in a range of from grea...

A carbon black is provided which is useful as an electrocatalyst carrier. The carbon black has a DBP oil absorption of 170 to 300 cm.sup.3/100 g, a specific surface area as measured by a BET method of 250 to 400 m.sup.2/g, a primary particle diameter value of 10 to 17 nm, and a total volume of open pores at the surface which have a pore radius of 10 to 30 nm of 0.40 to 2.0 cm.sup.3/g. The electrocatalyst can be used in electrochemical devices such as solid polymer electrolyte fuel cells.

Carbon bodies are heated in an oven under low pressure and while being swept with an inert gas, gaseous effluent containing elemental or compound sodium in sublimed form being continuously extracted from the oven via an effluent exhaust pipe. At least one sodium-neutralizing agent is injected into the effluent exhaust pipe immediately downstream from the outlet for exhausting gaseous effluent from the oven. The sodium-neutralizing agent is selected from carbon dioxide and steam, and it can be in...

Titanium dioxide nanoparticles are formed using a dispersing agent to form nanoparticles with desired size, shape, and uniformity. The titanium dioxide nanoparticles are formed by reacting an inorganic titanium compound with water or ice to form an aqueous titanium compound. The aqueous titanium compound is reacted or combined with a dispersing agent. Titanium dioxide nanoparticles are precipitated to form a suspension. The formation of the titanium dioxide nanoparticles is influenced by the pre...